Acrylic Waterproof Coating(UV resistance)
Description
Acrylic waterproof coating is made up of acrylic ester and many polymer emulsions. It is a kind of one-component waterborne environmental polymer waterproof coating material.
Environmental protection water-based formula. This materials can be applied at exposure roof and concealed roof. It enjoy great popularity by customers for its simple installation, materials is widely used in concrete, metal roofing, old roof repair, indoor waterproof etc.
Features
1.No solvent pollution, non-toxic and harmless, green and environment friendly.
2.Ready to use, it is suitable for engineering and home waterproofing.
3.Good performance on adhesion. It can be applied on wet or dry substrate.
4.Good water resistance and tensile property, high elasticity and low temperature flexibility.
5.High UV resistant, non-fading
Technical Data
|
No.
|
Item
|
Unit
|
Standard
|
Result
|
|
|
1
|
Solid Content
|
％
|
≥65
|
78
|
|
|
2
|
Tensile strength
|
MPa
|
≥1.0
|
1.8
|
|
|
3
|
Elongation at break
|
%
|
≥300
|
455
|
|
|
4
|
Flexibility at Low Temperature, Rod bent 180℃, ф10mm Stick
|
-
|
-10℃，No Crack
|
Pass
|
|
|
5
|
Water Impermeability, 0.3Mpa, 30min
|
-
|
Impervious
|
Pass
|
|
|
6
|
Heating Stretch rate
|
%
|
≤1
|
0.7
|
|
|
7
|
Drying time
|
Surface Dry
|
h
|
≤4
|
2
|
|
|
Fully dry
|
h
|
≤8
|
5
|
|
|
8
|
Tensile strength retention after treatment
|
Heat Treatment
|
%
|
≥80
|
105
|
|
|
Alkali Treatment
|
%
|
≥60
|
95
|
|
|
Acid Treatment
|
%
|
≥40
|
92
|
|
|
9
|
Elongation at break after treatment
|
Heat Treatment
|
%
|
≥200
|
326
|
|
|
Alkali Treatment
|
%
|
≥200
|
403
|
|
|
Acid Treatment
|
%
|
≥200
|
289
|
|
Package
20kg/pail
Recommended usage:
The usage for 1.5mm thickness coating is about 2.6kg/m2.
Storage
Should be stored at cool, dry and ventilated place; open storage and stacking are strictly prohibited; storage temperature no higher than 40ºC, storage period within 12 months.